Series 750
UVX
This product has been discontinued. Please contact your local sales representative for further assistance.
Generic Type
Aliphatic Acrylic Polyurethane
Common Usage
A user friendly, low VOC, aliphatic polyurethane coating that provides excellent color and gloss retention for exterior applications to steel, concrete and other substrates in commercial, industrial, and marine environments. Direct-to-Metal capability allows for a labor-saving, high-build, single coat application.
HAPS
Unthinned: 0.00 lbs/gal solids
Thinned 15% (No. 10 Thinner): 0.04 lbs/gal solids
Thinned 15% (No. 46 Thinner): 0.09 lbs/gal solids
Volume Solids
66.0 ± 2.0% (mixed) †
Colors
Refer to Tnemec Color Guide. Note: Certain colors may require multiple coats depending on method of application and finish coat color. When feasible, the preceding coat should be in the same color family, but noticeably different.
Finish
Semi-gloss
Primers
Steel: Self-priming or Series 1, 27, 66, L69, L69F, N69, N69F, V69, V69F, 90-75, 90-97, 90G-1K97, 91-H₂O, 93-H_2_O, 94-H₂O, 98-H₂O, 104, 132, 133, 135, 138, L140, L140F, N140, N140F, 141, 161, 394, 1220, 1224
Galvanized Steel & Non-Ferrous Metal: Series 66, L69, N69, V69, 1224. Note: For special galvanized surface preparation instructions, consult the latest version of Tnemec Technical Bulletin 10-78.
Concrete: Series 66, L69, L69F, N69, N69F, V69, V69F, L140, L140F, N140, N140F, 141, 161, 1224, 1254
CMU: Series 1254
Note: The following maximum recoat times apply; Series 141, 7 days; Series L69F, N69F, V69F, L140F, or N140F, 14 days; Series L69, N69, V69, L140, or N140, 21 days; Series 1, 27, 66, 104, 135, 161, 1254, 30 days; Series 132, 133 or 138, 90 days; Series 394, 1220, 1224, 12 months. Series 90-75, 90-97, 90G-1K97, 91-H₂O, 93-H_2_O, 94-H₂O, 98-H₂O, unlimited. Contact your Tnemec representative for specific recommendations.
Curing Time
| Temperature | To Touch | To Handle | To Recoat |
|---|---|---|---|
| 75°F (24°C) | 1-2 hours | 9 hours | 10-12 hours |
To resist moisture: 8 hours. Curing time varies with surface temperature, air movement, humidity and film thickness. Note: For faster cure in temperatures down to 35°F (2°C), add No. 44-456 Urethane Accelerator, see separate product data sheet for cure information. Note: The use of Series 44-456 accelerator is not recommended when temperatures exceed 75°F (24°C).
Volatile Organic Compounds
Unthinned: 0.73 lbs/gallon (88 grams/litre) (TBAc exempt)
Unthinned: 1.93 lbs/gallon (232 grams/litre)
Thinned 15% (No. 10 Thinner): 1.96 lbs/gallon (234 grams/litre) (TBAc exempt)
Thinned 15% (No. 10 Thinner): 2.79 lbs/gallon (335 grams/litre)
Thinned 15% (No. 46 Thinner): 0.81 lbs/gallon (97 grams/litre) (TBAc exempt)
Thinned 15% (No. 46 Thinner): 1.99 lbs/gallon (238 grams/litre)
Thinned 15% (No. 49 Thinner): 0.73 lbs/gallon (88 grams/litre) (TBAc exempt)
Thinned 15% (No. 49 Thinner): 1.93 lbs/gallon (232 grams/litre)
Number of Components
Two: Part A and Part B
Theoretical Coverage
1,059 mil sq ft/gal (26.0 m²/L at 25 microns). See APPLICATION for coverage rates. †
Recommended DFT
Topcoat Service: 2.0 to 5.0 mils (51 to 127 microns) per coat.
Direct-to-Metal; over Zinc or MIO-Zinc: 3.0 to 6.0 mils (76 to 154 microns)
Note: Number of coats and thickness requirements will vary with substrate, application method and exposure. For DTM or applications over zinc or MIO-zinc, consult the latest version of Tnemec Technical Bulletin 13-100 or contact your Tnemec representative.