Series 190
HullClad EC
Generic Type
Polyamide Epoxy
Common Usage
An epoxy primer that provides high levels of abrasion resistance and adhesion, as well as superior flexibility and resistance to seawater. Typically used as part of a corrosion-resistant antifoul bottom paint system on ship hulls.
View more product detailsContact your sales reps for quotes, problem solving advice, extensive technical knowledge, pricing, ordering and field support.
Primers
Steel: Self-priming
Volume Solids
73.0 ± 2.0% (mixed) †
Curing Time
At 4.0 mils (100 microns)
| Temperature || To Touch || To Overcoat |
|85°F (30°C) || 2 ½ hours min. || 5 hours min. |
| 68°F (20°C) || 4 hours min. || 9 hours min. |
| 50°F (10°C) || 11 hours min. || 19 hours min. |
|35°F (2°C) || 20 hours min. || 2 days min. |
---Curing time varies with surface temperature, air movement, humidity, and film thickness. Multiple coats may be required, please contact your Tnemec Representative for film thickness recommendations.
Theoretical Coverage
1,190 mil sq ft/gal (9.7 m²/L at 25 microns)
Number of Components
Two: Part A (Epoxy) and Part B (Hardener)
Recommended DFT
4.0 to 10.0 mils (100 to 255 microns) per coat.
Finish
Satin
Topcoats
Series N69, 72, 132, 191, 194, 195, 690, 1070, 1090, 1094. Note: The following maximum recoat times apply: Series 1070, 1090, 1094, 7 days; Series 72, 21 days; Series N69, 690, one month.
Volatile Organic Compounds
Unthinned: 2.38 lbs/gallon (286 grams/liter)