Series 27WB
Typoxy
This product has been discontinued. Please contact your local sales representative for further assistance.
Generic Type
Inorganic Hybrid Water-Based Epoxy
Common Usage
A unique, low odor, low VOC, water-based epoxy coating featuring HydroLink curing technology for exceptional durability and corrosion resistance. Used for the protection and finishing of steel and concrete structures including structural steel, tanks, pipes, and equipment. Superior wetting for marginally prepared steel and tightly adhered existing coatings. This coating is ideally suited for steel fabrication and OEM applications, with fast-curing and rapid handling properties. Series 27WB exhibits low yellowing and good color stability in whites and light tone colors. Formula protected under U.S. patent.
Special Qualifications
Series 27WB was tested in accordance with, and passed, the California Department of Public Health CDPH/EHLB/Standard Method Version 1.1, 2010 emissions testing and meets qualifications of LEED v4, Collaborative for High Performance Schools, and Living Building Challenge.
Finish
Satin
Volume Solids
100% (mixed) †
HAPS
0 lbs/gal solids
Volatile Organic Compounds
Unthinned: 0.01 lbs/gallon (0.9 grams/litre) †
Number of Components
Two: Part A and Part B (One Part A to One Part B by volume.)
Theoretical Coverage
1,604 mil sq ft/gal (39.4 m²/L at 25 microns). See APPLICATION for coverage rates. †
Recommended DFT
3.0 to 14.0 mils (75 to 350 microns) per coat. Note: Number of coats and thickness requirements will vary with substrate, application method and exposure. Contact your Tnemec representative.
Colors
1255 Beige, 00WH Tnemec White, 39BL Delft Blue, 35GR Black, 33GR Gray. Other colors may be available, contact your Tnemec representative. Note: This coating can exhibit color change when subjected to sunlight. If this coating is being used as a finish coat, and exposed to UV light in exterior exposure, caution should be taken when selecting colors. Contact your Tnemec representative for more information.
Primers
Steel: Self-priming or Series 1, 66, 66HS, L69, L69F, N69, N69F, 90G-1K97, 90-97, H90-97, 91-H₂O, 94-H₂O, 161, 161HS, 394. Note: Series 1, 90G-1K97, 90-97, H90-97, 91-H₂O, 94-H₂O and 394 must be exterior exposed for 24 hours prior to topcoating.
Galvanized Steel: Self-priming
Concrete: Self-priming, 215, 217, 218, 1254
CMU: Self-priming, 130, 215, 1254
Drywall: Self-priming, 151
Topcoats
Series 30, 66HS, 72, 73, 113, 114, 115, 156, 157, 158, 161HS, 180, 181, 270, 273, 280, 281, 287, 290, 291, 297•, 406, 435, 436, 446, 740, 750, 1026, 1028, 1029, 1070, 1070V, 1071, 1071V, 1072, 1072V, 1074, 1074U, 1075, 1075U, 1077, 1078, 1080•, 1081•. Note: When topcoating with Series 740 or 750 over 27WB, a 90 day maximum recoat time applies. •An extended cure time is needed when topcoating with Series 297, 1080 or 1081. Reference additional recoat times listed below the cure table. Note: More than one finish coat may be required to achieve uniform and desired gloss level.
Curing Time
| Temperature | To Touch | To Handle | To Recoat† |
|---|---|---|---|
| 120°F (49°C) | 15 minutes | 1 hour | 2 hours |
| 95°F (35°C) | 30 minutes | 2 hours | 3 hours |
| 75°F (24°C) | 1 hour | 6 hours | 8 hours |
| 55°F (13°C) | 2 hours | 8 hours | 16 hours |
| 45°F (7°C) | 3 hours | 10 hours | 24 hours |
| 35°F (2°C) | 4 hours | 3 days | 4 days |
Curing time varies with surface temperature, air movement, humidity and film thickness. For immersion service cure a minimum of 24 hours at 75°F (24°C). † The following minimum recoat times apply when topcoating with Series 297, 1080 or 1081: 95°F (35°C) 12 hours, 75°F (24°C) and 55°F (13°C) 24 hours, 45°F (7°C) 4 days, 35°F (2°C) 7 days. Note: For faster cure in temperatures down to 35°F (2°C), add No. 44-700 Epoxy Accelerator, see separate product data sheet for cure information. Note: The use of Series 44-700 Accelerator is not recommended when temperatures exceed 75°F (24°C).